Expanded PTFE with Graphite

Description and Application

Style 2007 packing is an interlock braid, utilizing TEADIT’s EG8G-S PTFE/graphite yarn and a high temperature break-in lubricant. EG8G-S yarn is formed from expanded PTFE in which fine particles of pure graphite have been encapsulated. The resulting packing combines the chemical resistance of PTFE with the heat dissipation characteristics of graphite, thus allowing much higher shaft speeds than conventional PTFE packings.

Style 2007 is chemically inert over the entire 0-14 pH range with these exceptions: molten alkali metals, flourides, aleum, fuming nitric acid, aqua regia, and other strong oxidizing agents.

This style is an excellent general service and corrosive service packing. It is commonly used in pumps, valves, rotating and reciprocating shafts, mixers and agitators, and is especially designed for services involving surface speeds and temperatures higher than those that can be handled by pure PTFE packing.

Service Limits

Temperature ºF (ºC)
Minimum -328 (-200)
Maximum 536 (280)
Pressure psi (bar)
Static 2900 (200)
Rotating 507 (35)
Reciprocating 1450 (100)
Minimum 0
Maximum 14
Shaft Speed f/m (m/s)
Maximum 4921 (25)

Approximate Yields (+/-10%)

Size Ft/Lb 84 37.8 20.2 13.7 9.8 7.4 5.2 4.2 3.5 2.5 1.9 1.4
Inch 1/8 3/16 1/4 5/16 3/8 7/16 1/2 9/16 5/8 3/4 7/8 1
Package 1 Lb (0.5kg) 2 Lbs (1kg) 5 Lbs (2kg) 10 Lbs (5kg)

STYLE 2007*

graf 2007G

*Tests conducted in laboratory, simulating real application conditions as compared with competitor's packing.



Datasheet STYLE 2007





10545 Red Bluff Road, Pasadena, TX 77507
Phone: (281) 476-3900 - Fax: 281-476-3999 – TOLL FREE: 800-999-0198

2015© Teadit | All Material Copyright are reserved.


This website uses modern technologies such as JavaScript, CSS, HTML5 and WebFonts; because of this, it is best viewed in modern browsers.

We recommend to use Google Chrome as your primary browser for this website.